All About Flex: Lead-Free Soldering Flexible Circuits


Reading time ( words)

Ever since the European community adopted the RoHS directive in 2006, the U.S. electronics industry has been steadily increasing its use of lead-free solder. Medical was the first U.S. industry to go totally lead-free. Today, a significant percentage of electronics soldering is done with lead-free solder. After several years of refinement and withstanding some mischaracterizations, lead-free soldering is proving to be cost effective and reliable.

While lead-free solder is reliable, there are differences in materials and processing that need to be understood to ensure a robust electronics design.

Material Composition: The most widely used lead-free solder paste is a tin/silver/copper alloy (Sn/Ag/Cu). These are available in slightly different combinations; the following are the more common ones:

  • Sn96.5/Ag3.0/Cu0.5
  • Sn95.5/Ag3.8/Cu0.7
  • Sn95.5/Ag4.0/Cu0.5

There are alloys other than tin/silver/copper that can be used for lead-free soldering; most of these are for non-electronic applications. The optimal choice of alloy depends on the type of surface to solder and the application for the flexible circuit.

Cosmetic Appearance: The classic tin-lead solder joints were shiny and smooth. In fact, a defective solder joint often had a dull, rough appearance. This is not the case for lead-free solder joints, which have a less shiny appearance. Those who are not familiar with lead-free solder will immediately flag the dull appearance as defective joints. The dull appearance in solder joints is not indicative of the quality of the solder joint, but simply due to the inherent properties of the alloy.  See Figure 1 for a side-by-side comparison.

Lead_Free.jpg 

Figure 1: Lead-free vs. tin-lead. (Source: CEDOS Electronics)

Process Temperature:  Lead-free solder starts to reflow around 218°C, whereas tin-lead solder will reflow around 188°C. The higher temperature can have an adverse impact on the fixtures, equipment and materials used on a flexible circuit. When introducing a new part number requiring lead-free solder, an engineering review should occur to insure all materials have proper temperature compatibility.

Mechanical Strength: Lead-free solder does not have the mechanical strength of the traditional tin-lead solder. This is one of the reasons that the lead-free is not used in military or aerospace applications. The RoHS directive exempts military and some aerospace products. While tin-lead solder has better mechanical properties, there are ways to address mechanical strength issues with lead-free solder.   Adding epoxy or conformal coating to reinforce the bond areas are ways to add robustness to designs requiring a high level of mechanical strength.

Flux: As with tin-lead soldering, there are two basic types of fluxes used with lead-free soldering: water washable flux and no-clean flux. The water washable flux must be completely removed after soldering. Water wash generally works well if there is adequate room under the components to rinse away residue. If the component density and profile do not allow thorough rinsing, then no-clean flux should be used. No-clean flux leaves a visible residue, which some may find objectionable. There may be a temptation to require residue removal with a cleaning process. But experts advise against removing the residue of a no-clean flux. No-clean flux residue is designed to encapsulate any contaminants that could potentially cause electrical problems in the field. By cleaning the no-clean flux, there is risk some of the contaminants will remain and create potential reliability problems.

Testing: Reliability and electrical testing are the same for both lead-free and tin-lead soldering processes. There are a couple of tests to determine if a given component has lead. One is to apply a chemical that simply changes color if there is lead in the solder. One could also use an atomic absorption spectrophotometer that will provide the exact content of the metal. These tests are mainly applicable to ensure an incoming product is lead-free, or to prove that a product meets RoHS requirements. During circuit fabrication, in-process material control should insure solder paste is lead-free.

An electronic packaging designer who is unfamiliar with lead-free processes will need to be educated on the various design, material, process, component and inspection nuances that lead-free soldering presents. Many circuit suppliers are able to provide a significant amount of design support for applications requiring lead-free solder. 

 

Dave Becker is vice president of sales and marketing at All Flex Flexible Circuits LLC.

Share

Print


Suggested Items

Future Trends in Flying Probe Testing

11/29/2019 | I-Connect007 Editorial Team
Peter Brandt, director of sales for Europe and Japan at atg, sits down with Pete Starkey and Barry Matties, gives his views on market requirements and testing technologies, and explains how flying probe testing is becoming the industry standard at all levels of production—and in many cases, the only practicable solution.

Decreasing Bend Radius and Improving Reliability- Part II

11/22/2019 | Kelsey Smith, All Flex
Many of the issues that arise when using a flex circuit come from a lack of knowledge about how to properly design one, especially when the circuit is required to bend. Many novices will design a circuit that calls for bending the flex in too tight of a bend radius, which can cause damage to the circuit and lower the reliability of the end product. This series of articles will focus on the seven key aspects to consider when designing for maximum durability and maximum “flexibility”.

Solder Mask Tack Dry

11/08/2019 | Nikolaus Schubkegel
As a general rule, the tack-dry temperature should be as low as possible; in other words, it should only be as high as necessary. If the temperature is too low, the evaporation rate for the solvent will be to slow, and the solder mask will not dry in a reasonable amount of time. If the temperature is too high, however, the dry time certainly will be excellent, but it could create a solder mask lock-in with repercussions by the developing time.



Copyright © 2019 I-Connect007. All rights reserved.