Controlling the ENIG Process for Optimum Efficiency and Performance


Reading time ( words)

Introduction

In last month’s Trouble in Your Tank, different levels of corrosion in the nickel deposit were presented. In addition, the suggestion was made that mid-phosphorous content EN process was more beneficial with respect to solderability, as opposed to a high phos content nickel deposit. Certainly, concerns with corrosion of the nickel (with lower phos) were allayed as long as the proper process controls were in place. Ideally, the ENIG process must provide the optimum in solder joint reliability while operating at the highest level of cost efficiency. All too often, process parameters that have the most influence on these critical attributes are poorly understood. An example of poor control is shown in Figure 1. The gold deposit has been removed in order to expose the electroless nickel surface.

It is very difficult to discern any anomalies in the nickel deposit without removing the gold. It is clear from the SEMs in Figure 1 that there is significant corrosion on the electroless nickel surface. Obviously, this is an unacceptable situation, and in order to prevent it one must work harder to optimize and control the electroless nickel-immersion gold process. Some of these factors will now be presented in detail.

Critical Electroless Nickel Features:

  1. Phosphorous content control in the electroless nickel deposit. Don’t underestimate this important parameter.
  2. Stabilizers in the EN solution influence phosphorous content in the deposit.
  3. Phos content has strong influence on solderability, immersion gold deposit thickness and potential for hyper-corrosion.

Let’s look at these points in a little more detail.

As I have written in this monthly column on many occasions, operating the chemical processes within the process window is the key to consistent and predictable performance. After all, your customers should expect no less from you. So with respect to #1 above, it is recommended that the EN process be able to maintain a reasonably tight window with respect to phos content through five metal (MTOs) turnovers in the nickel solution.

Read the full column here.


Editor's Note: This column originally appeared in the August 2014 issue of The PCB Magazine.

Share




Suggested Items

A Conversation with Canice Chung, TTM Technologies

12/09/2014 | Barry Matties, I-Connect007
We had the opportunity to sit down with Canice Chung, Executive Vice President of TTM Technologies, Inc. to discuss the current trends and challenges of PCB Manufacturing in China.

A Conversation with Laurent Nicolet, Schmid Group

12/07/2014 | Barry Matties, I-Connect007
During the HKPCA & IPC Show 2014, Laurent Nicolet, VP - PCB Business Unit of Schmid Group took a few minutes to discuss the automation technology that was on display and share the changes he's seen in the China market.

Thin PCBs for Smart Phones: Technology and Reliability Considerations

11/19/2014 |
The next generation of smartphones will demand very thin multilayer boards to reduce product thickness. This paper shows three different manufacturing approaches which can be used for very thin, any-layer build-ups. The technological approaches are compared on reliability level--the any-layer copper filled microvia technology which is to be considered state-of-the-art for high-end phones and the ALIVH-C/G technology well established in Japan.



Copyright © 2023 I-Connect007 | IPC Publishing Group Inc. All rights reserved.